(1) Bitumina
i) Medium Curing Cutback Grade MC-30 (ASTM D2027-97)
Parameters Unit Min Max Test Method
Kinematic Viscosity at 60°C (140°F) mm2/s 30 60 ASTM D2170
Flash Point (Tag Open -cup) °C (°F) 38(100) ---- ASTM D3143
Distillation Test: (Distillate, volume percent of total distillate to 360°C (680°F)
- To 225°C (437°F) % ---- 25 ASTM D402
- To 260°C (500°F) % 40 70
- To 316°C (600°F) % 75 93
- Residue from distillation to 360°C (680°F) % 50 ----
Tests on residue from distillation:
Viscosity at 60°C (140°F) Pa∙sA 30 120 ASTM D5
Ductility at 25°C (77°F) cm 100 ---- ASTM D113
Solubility in trichloroethylene % 99.0 ---- ASTM D2042
Water % ---- 0.2 ASTM D95
AInstead of viscosity of the residue, the specifying agency, at its option, can specify penetration 100g: 5s at 25°C (77°F) of 120 to 250 for Grades MC-30, MC-70, MC-250, MC-800 and MC-3000. However, in no case will both be required.
ii) Rapid Curing Cutback Grade RC-70 (ASTM D2028-97 Revised 2004)
Parameters Unit Min Max Test Method
Kinematic Viscosity at 60°C (140°F) mm2/s 70 140 ASTM D2170
Flash Point (Tag Open -cup) °C (°F) ---- ---- ASTM D3143
Distillation Test: (Distillate, volume percent of total distillate to 360°C (680°F)
- To 190°C (374°F) % 10 ---- ASTM D402
- To 225°C (437°F) % 50 ---- ASTM D402
- To 260°C (500°F) % 70 ----
- To 316°C (600°F) % 85 ----
- Residue from distillation to 360°C (680°F) % 55 ----
Tests on residue from distillation:
Viscosity at 60°C (140°F) Pa∙sA 60 240 ASTM D5
Ductility at 25°C (77°F) cm 100 ---- ASTM D113
Solubility in trichloroethylene % 99.0 ---- ASTM D2042
Water % ---- 0.2 ASTM D95
AInstead of viscosity of the residue, the specifying agency, at its option, can specify penetration 100g: 5s at 25°C (77°F) of 80 to 120 for Grades RC-70, RC-250, RC-800 and RC-3000. However, in no case will both be required.
(2) Jey Oil Company
Grade MC-250 Test Method
Properties Min Max
Kinematic Viscosity at 60°C (140°F), mm2/s 250 500 ASTM D2170
Flash Point (Tag Open -cup), °C (°F) 66(150) ---- ASTM D3143
Distillate test: Distillate, volume percent of total distillate to 360 °C (680 °F)
To 225 °C (437 °F) ---- 10 ASTM D402
To 260 °C (500 °F) 15 55
To 316 °C (600 °F) 60 87
Residue from distillation to 360°C (680°F), percent volume by difference 67 ----
Tests on residue from distillation:
Penetration at 25 °C (77 °F), 100 gr, 5 s 120 250 ASTM D5
Ductility at 25°C (77 °F), cm 100 ---- ASTM D113
Solubility in trichloroethylene, (% by mass) 99.0 ---- ASTM D2042
Water, (% by volume) ---- 0.2 ASTM D95
(3) Chinese Requirement
Parameters Unit Typical Method
Density @15°C 密度 kg/l 0.9471 ASTM D1298
Viscosity @50°C 运动粘度 mm2/s 122.0 ASTM D445
Total Sulfur 全硫 % (m/m) 2.24 ASTM D4294
Asphaltene 沥青分 %wt 10.3 IP143
Water by distillation 水分 % (v/v) 0.1 ASTM D95
MCR 残炭 % (m/m) 14.0 ASTM D189
Ash 灰分 % (m/m) 0.074 ASTM D482
Stimulated Distillation
140°F~225°F (60~107°C) Wt% 8.60 ASTM D7169
225°F~305°F (107~152°C) Wt% 10.90
305°F~390°F (152~199°C) Wt% 12.80
390°F~480°F (199~249°C) Wt% 16.50
480°F~600°F (249~316°C) Wt% 24.40
600°F~700°F (316~371°C) Wt% 32.90
道路沥青的来源??
答：沥青是石油炼化的产品.简单说石油炼化企业在炼化原油时,过去主要生产气和汽,煤,柴油,剩下的重油再加工就是沥青,但现在路面对沥青要求高了,原油加工沥青时不再象过去那样子用原油炼化后的垃圾了.而是直接用原油或燃料油进行加工.得到的道路沥青质量较好.目前国内中石油,中石化的炼厂基本都有生产.也有进口...
进口稀释沥青报关需要走哪些步骤行业新闻资讯
答：quality/quantity/weight F：MSDS(化工品安全成分说明书）1、我司负责中国港口的换单、清关事宜 2、我司安排送货到客户手中 沥青进口报关单证：1、正本提单或仓单 2、商业票据（复印件）3、装箱单（复印件）4、原产地证明（复印件）5、合同（复印件）7、付汇情况表另：货物到港后需在14天内报关 ...
稀释沥青的方法?
答：沥青溶于二甲苯、二氯甲烷和四氯乙烯等烃类，芳香烃稀释降低粘度效果最好。
稀释沥青的方法
答：稀释沥青的方法有二种：1、掺配，即用较稀的沥青掺入，使沥青得到稀释。2、掺入稀释剂，一般使用柴油；汽油也行，但汽油易恽发，易燃烧，使用时要注意安全。稀释而成的沥青产品称为液体沥青，也称轻制沥青或稀释沥青。沥青的软化点高，在溶剂中不易溶化，溶融温度亦较高，调配时不安全。液体石油...
SBS改性沥青哪种牌子好?国产的好还是进口的好?一般一级高速公路采用那种...
答：改性沥青采购根据属地进行采购。比如东北的肯定采购盘锦附近的加工厂，这个能够达到设计指标就可以。也可以进行现场改性。现场改性需要独秀改性沥青设备，欢迎咨询。
一大批新规来了!6月1日起这些细节不注意可能会“犯法”
答：一是归入税则号列27075000,且200摄氏度以下时蒸馏出的芳烃以体积计小于95%的进口产品,主要包括“混合芳烃”;二是归入税则号列27079990、27101299的进口产品,主要包括“轻循环油”;三是归入税则号列27150000,且440摄氏度以下时蒸馏出的矿物油以体积计大于5%的进口产品,主要包括“稀释沥青”。《公告》仅涉及消费税的征...
为何目前我国没有广泛使用冷拌沥青混合料用于公路工程
答：你好，首先冷拌沥青混合料也叫乳化沥青混合料，那么一般的基质沥青是需要热拌的。热拌沥青工艺比较复杂，要将集料加热，沥青加热，所以它必须在一个非常固定的场所拌制。另外我们知道我国高等级路面都是采用热拌沥青混合料，它的施工很成熟，不需要养护，压实后就可通车。乳化沥青混合料根据规范只能用于...
进口稀释沥青报关注意事项有哪些
答：注意安全 注意实报 分析报告 检验检疫
...由于制备或采购乳化沥青困难,需制备稀释石油沥青
答：也可以用柴油来稀释效果一样的。比例跟制备也是很简单的（沥青加温的130度左右之间 加入柴油搅拌即可或者采用沥青泵打循环的方式也可以，这个要根据沥青多少来取决与搅拌时间及循环时间了）你所说的效果不理想应该是搅拌不均匀和掺配比例不合适造成的，这种工艺在几十年前就在使用，现在很少用主要是成本太...
用机油稀释沥青行吗
答：可以的 下面是节选一篇文章片段 目前，国内外的废润滑油处理技术均不高，规模偏小，全世界的废油回收率在10％左右，我国废油回收率只有6％左右 ，国内外废润滑油的主要去向有以下4种路径：焚烧或直接废弃，流人下水道、河流、荒地；废润滑油经脱重金属后作为燃料或用作沥青稀释剂、高硫燃料掺和剂...